Photocatalytic Activity of Nanocoatings Based on Mixed Oxide V-TiO2 Nanoparticles with Controlled Composition and Size

Résumé

V-TiO2 photocatalyst with 0 ≤ V ≤ 20 mol% was prepared via the sol–gel method based on mixed oxide titanium–vanadium nanoparticles with size and composition control. The mixed oxide vanadium–titanium oxo-alkoxy nanonoparticles were generated in a chemical micromixing reactor, coated on glass beads via liquid colloid deposition method and underwent to an appropriate thermal treatment forming crystallized nanocoatings. X-ray diffraction, Raman, thermogravimetric and differential thermal analyses confirmed anatase crystalline structure at vanadium content ≤ 10 mol%, with the cell parameters identical to those of pure TiO2. At a higher vanadium content of ~20 mol%, the material segregation began and orthorhombic phase of V2O5 appeared. The crystallization onset temperature of V-TiO2 smoothly changed with an increase in vanadium content. The best photocatalytic performance towards methylene blue decomposition in aqueous solutions under UVA and visible light illuminations was observed in V-TiO2 nanocoatings with, respectively, 2 mol% and 10 mol% vanadium.
Fichier principal
Vignette du fichier
39_V-TiO2-catalysts-2021.pdf (18.68 Mo) Télécharger le fichier
Origine : Publication financée par une institution

Dates et versions

hal-03845775 , version 1 (09-11-2022)

Identifiants

Citer

Miguel Sanchez Mendez, Alex Lemarchand, Mamadou Traore, Christian Perruchot, Capucine Sassoye, et al.. Photocatalytic Activity of Nanocoatings Based on Mixed Oxide V-TiO2 Nanoparticles with Controlled Composition and Size. Catalysts, 2021, 11 (12), pp.1457. ⟨10.3390/catal11121457⟩. ⟨hal-03845775⟩
24 Consultations
33 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More